Researchers have discovered a swirling fluidlike behavior in a solid piece of metal sliding over another, providing new insights into the mechanisms of wear and generation of machined surfaces that could help improve the durability of metal parts. Studies using a microscope and high-speed camera revealed the formation of bumps, folds, vortex-like features and cracks on the metal surface. The findings were surprising because the experiment was conducted at room temperature and the sliding conditions did not generate enough heat to soften the metal.
"We see phenomena normally associated with fluids, not solids," said Srinivasan Chandrasekar, a professor of industrial engineering at Purdue University, working with postdoctoral research associates Narayan Sundaram and Yang Guo.
Numerous mechanical parts, from bearings to engine pistons, undergo such sliding.
"It has been known that little pieces of metal peel off from sliding surfaces," Chandrasekar said. "The conventional view is that this requires many cycles of rubbing, but what we are saying is that when you have surface folding you don't need too many cycles for these cracks to form. This can happen very quickly, accelerating wear."
Findings are detailed in a research paper published in the Sept. 7 issue of the journal Physical Review Letters.
The researchers are developing models to further study the phenomena and understand the wide-ranging consequences of such fluidlike flow in metals, Chandrasekar said. The findings might also lead to improved surface quality in materials processing.
The team observed what happens when a wedge-shaped piece of steel slides over a flat piece of copper. It was the first time researchers had directly imaged how sliding metals behave on the scale of 100 microns to1 millimeter, known as the mesoscale.
The observations show how tiny bumps form in front of the steel piece, followed by the swirling vortex-like movement and then the creation of shallow cracks. The folding and cracking were most pronounced when the steel piece was held at a sharp angle to the copper surface.
The researchers hypothesize that the folding and cracking is due in part to a phenomenon similar to "necking," which happens as a piece of metal is stretched.
Researchers used a specialized laboratory setup that included a high-speed camera and equipment that applies force to the sliding metals. The behavior was captured in movies that show the flow in color-coded layers just below the surface of the copper specimen. Copper is commonly used to model the mechanical behavior of metals.
"Researchers have never had a good experimental setup to observe this kind of deformation directly," Guo said. "Our setup enables us to see the entire history of this fluidlike behavior as it occurs, whereas more conventional experiments rely on still images taken after the experiment is finished."
Metals are made of groups of crystals called grains. Metal surfaces that have smaller grains may be less susceptible to the folding and crack formation.
"We need to explore what role grain size plays," Chandrasekar said. "We think there should be some grain size below which this folding mechanism may be less active. We need to explore why, under what conditions, solid metals behave like fluids."
Purdue University: http://www.purdue.edu/
This press release was posted to serve as a topic for discussion. Please comment below. We try our best to only post press releases that are associated with peer reviewed scientific literature. Critical discussions of the research are appreciated. If you need help finding a link to the original article, please contact us on twitter or via e-mail.